Several specimen of TUBS-M and TUBS-T were sintered at different temperatures with same holding times in order to investigate the influence of the sintering temperature on the thermal properties.

The cast green specimens were air-sintered at 1000 C, 1050 C, 1100 C or 1150 C for 2 h in a box furnace, with both heating and cooling rates fixed at 3 C/min.

Improve CS from 7 to 20 MPa [129]

The sintering procedure used in this work was developed using a range of terrestrial lunar regolith simulants with varying compositions

The present sintering experiments were all performed at the same maximum temperature (1100 C; i.e., below

The thermal diffusivity () of the molten and SPSed samples was determined using the laser flash method in a flowing Ar atmosphere (Netzsch LFA 467 HT, Netzsch Analyzing & Testing, Shanghai, China).

In this study, the HUST-1 lunar regolith simulant (HLRS) was sintered at 1030, 1040, 1050, 1060, 1070, and 1080 C.

the flash sintering process was investigated for the first time to realize the sample forming of HUST-1 lunar regolith simulant (LRS).